This is t9064 titanium.... I am gonna try this insert in my homemade frameback... It is incredibly hard.. White Sparks off the grinder... When heat treated it will go up to 80hrc... Oughta be fun to hone....Lol... More of this story to come...
See you in March 2015....When you're done honing!
Paco Titanium DE Blades 5 pack for $200? Please don't over-glue the wax paper.
What was the blade before? What is it? Very neat. Lolks cool!
>This is t9064 titanium....
What else is in this Ti alloy? I assume you are heat treating into the alpha-beta phase for hardness? I am curious as to why you chose this alloy, and how you specifically plan to treat it.
Subscribed, if for no other reason than to witness Paco's declining mental state through the honing process.
[FONT=Arial, Arial, Helvetica] [/FONT] [FONT=Arial, Arial, Helvetica]Chemistry Limits (%)[/FONT] |- | [FONT=Arial, Arial, Helvetica]Al[/FONT] | [FONT=Arial, Arial, Helvetica]2.50 - 3.50[/FONT] | |
[FONT=Arial, Arial, Helvetica]V[/FONT] | [FONT=Arial, Arial, Helvetica]2.00 - 3.00[/FONT] | ||
[FONT=Arial, Arial, Helvetica]O[SUB]2[/SUB] Max[/FONT] | [FONT=Arial, Arial, Helvetica]0.12[/FONT] | ||
[FONT=Arial, Arial, Helvetica]Fe Max[/FONT] | [FONT=Arial, Arial, Helvetica]0.30[/FONT] | ||
[FONT=Arial, Arial, Helvetica]H[SUB]2[/SUB] Max[/FONT] | [FONT=Arial, Arial, Helvetica]0.015[/FONT] | ||
[FONT=Arial, Arial, Helvetica]C Max[/FONT] | [FONT=Arial, Arial, Helvetica]0.05[/FONT] | ||
[FONT=Arial, Arial, Helvetica]N[SUB]2[/SUB] Max[/FONT] | [FONT=Arial, Arial, Helvetica]0.02[/FONT] |
[FONT=Arial, Arial, Helvetica]Mechanical Properties[/FONT] |- | [FONT=Arial, Arial, Helvetica] [/FONT] | [FONT=Arial, Arial, Helvetica]Annealed Condition[/FONT] | [FONT=Arial, Arial, Helvetica]Cold Worked and Stress Relieved[/FONT] | ||
[FONT=Arial, Arial, Helvetica]Ultimate Tensile Strength - ksi[/FONT] | [FONT=Arial, Arial, Helvetica]90[/FONT] | [FONT=Arial, Arial, Helvetica]125[/FONT] | |||
[FONT=Arial, Arial, Helvetica]Yield Strength - ksi[/FONT] | [FONT=Arial, Arial, Helvetica]70[/FONT] | [FONT=Arial, Arial, Helvetica]105[/FONT] | |||
[FONT=Arial, Arial, Helvetica]Elongation %[/FONT] | [FONT=Arial, Arial, Helvetica]15[/FONT] | [FONT=Arial, Arial, Helvetica]10[/FONT] |
[FONT=Arial, Arial, Helvetica] [/FONT] [FONT=Arial, Arial, Helvetica]Physical Properties[/FONT] |- | [FONT=Arial, Arial, Helvetica] [/FONT] | [FONT=Arial, Arial, Helvetica] [/FONT] | |
[FONT=Arial, Arial, Helvetica]Density (lbs/in[SUP]3[/SUP])[/FONT] | [FONT=Arial, Arial, Helvetica]0.162[/FONT] | ||
[FONT=Arial, Arial, Helvetica]Elastic Modulus (x10[SUP]6[/SUP] psi)[/FONT] | [FONT=Arial, Arial, Helvetica]14.5[/FONT] | ||
[FONT=Arial, Arial, Helvetica]Beta Transus Temp ([SUP]o[/SUP]F)[/FONT] | [FONT=Arial, Arial, Helvetica]1715[/FONT] | ||
[FONT=Arial, Arial, Helvetica]Weldability[/FONT] | [FONT=Arial, Arial, Helvetica]Good[/FONT] |
this experiment is on hold for a bit.....